Technical Specifications

Physical properties
STANDARD
Test conditions
UNITS
Density
SO 1183
Sintered test sample
g/cm³
1.2
Water absorption 23 °C / 24 h
MPTS ISO 3167 A
%
<0.5
Melt volume-flow rate MVR 170 °C/2,16 kg
SO 1133
Granulate
cm³/10 min
10
Mechanical properties
Normklima NK 23 °C/50% rel. Luftfeuchtigkeit, meassured on sintered parts
Shore hardness A
ISO 868
92
Flexural Modulus (x-direction)
DIN 53504
SLS-tensile bar Tyep S1
MPa
9
Flexural Modulus (z-direction)
DIN 53504
SLS-tensile bar Tyep S1
MPa
10
Tensile Strength (x-direction)
DIN 53504
SLS-tensile bar Tyep S1
MPa
27
Tensile Strength (z-direction)
DIN 53504
SLS-tensile bar Tyep S1
MPa
22
Strain at break (x-direction)
DIN 53504
SLS-tensile bar Tyep S1
%
400
Strain at break (z-direction)
DIN 53504
SLS-tensile bar Tyep S1
%
370
Abrasion resistance (x-direction)
ISO 4649
Sintered test sample
mm³
31
Abrasion resistance (z-direction)
ISO 4649
Sintered test sample
mm³
28
Thermal properties
Vicat-softening temperature VST A
DIN ISO 306
MPTS ISO 3167 A
°C
90
Melting temperature
DIN ISO 306
°C
160
Electrical properties
Insulating resistance Bar elektrode R25
DIN/IEC 60167
MPTS ISO 3167 A
>1012
Surface resistance ROB
DIN IEC 60093
Ronde 60 x 4 mm
>1012