Hi
Which plastic material would be best suited to create an airtight part?
The description of Polyamide states that it is slightly porous but has a lower porosity that parts produced with laser sintering. Does the same apply to Rubber-like (MJF)?
Thank you for the help in advance!
Best,
David
Hi David,
I would suggest MJF because it’s more likely to be airtight. Sealing as a finish could also help.
Rubber-like is built in the same process as Polyamide on MJF so it has the same effect.
Although it is hard to guarantee as it also depends on pressure, temperature, duration etc.
I hope the above is useful to you.
Should you need any further information, please do not hesitate to contact us:https://imaterialise.helpjuice.com/contact-us?contact_query=Please%20enter%20your%20question
Best regards,
Anna
Hi Anna,
thank you for your reply, I will try that out!
Best,
David